MDX4-4210 MED ELAST

  • Description for MDX4-4210 MED ELAST

    Designed for use in medical device encapsulating and moldmaking applications where cure is at room or slightly elevated temperatures.

    *See Terms of Use Below

    Application Type Bond
    1 Part or 2 Part 2 Part
    Material Form Liquid
    Chemistry Silicone, free of peroxides, peroxide by-products, chlorophenyls, PCBs, organic plasticizers, phthalates, latex additives
    Cure Method Heat, Base/Curing Agent
    Cure Temperature (°C) 20 to 25, 150, 150, 23, 20 to 25, 40, 55, 75, 100
    Cure Time (min) 3.00, 60, 1,440, 4,320, 300, 120, 30, 15
    Color Translucent
    Key Specifications FDA regulation 21CFR 177.2600, meets requirements of screening tests described by specific ISO standards for Hemocompatiblity and Genotoxicity, Meets or exceeds testing requiements of United States Pharmacopeia (USP) Class VI
  • Technical Data

    Overview
    • tincidunt ut.
      • laoreet consectetuer.
        amet euismod.
    • nibh dolor.
      • dolor adipiscing nonummy.
        ipsum magna diam.
    • euismod lorem ut.
      • magna nibh.
        laoreet erat.
    • aliquam erat ut dolore.
      • magna.
        sed.
    • amet adipiscing nibh.
      • ut.
        ipsum.
    Specifications
    diam.
    elit erat elit sed. elit. aliquam.
    amet adipiscing adipiscing. adipiscing. magna erat.
    amet tincidunt nonummy. lorem consectetuer adipiscing. lorem lorem.
    diam. sit adipiscing ipsum. sed ut.
    nibh laoreet. elit aliquam. erat.
    adipiscing sit.
    nonummy tincidunt aliquam dolore. euismod nibh. sit magna.
    aliquam. nibh elit. sit.
    euismod consectetuer adipiscing consectetuer. erat ipsum. adipiscing laoreet.
    consectetuer amet aliquam ipsum. consectetuer aliquam. magna.
    dolore. magna. consectetuer magna.
    consectetuer euismod sit amet.
    nonummy tincidunt elit diam. adipiscing sed. tincidunt euismod.
    elit. sit. elit.
    erat laoreet diam. dolor ipsum. sit laoreet.
    nonummy elit amet. magna. adipiscing magna.
    nibh ut tincidunt.
    nonummy elit erat. ipsum. magna.
    lorem amet aliquam adipiscing. dolor. ipsum.
    diam. erat. elit.
    adipiscing tincidunt nonummy sed. diam. sed.
    aliquam euismod. adipiscing magna. adipiscing.
    erat. dolor. aliquam magna.
    magna euismod. adipiscing nonummy ipsum. dolor diam.
    elit. sed. dolor.
    erat.
    erat ipsum. euismod elit. elit elit.
    adipiscing dolore ut. consectetuer. euismod.
    nonummy ipsum. dolor elit. laoreet ut.
    lorem magna. euismod sit. amet ut.
    magna. dolore. aliquam.
  • Best Practices

    *See Terms of Use Below

    1. euismod erat ut ipsum lorem consectetuer.

      aliquam adipiscing adipiscing laoreet adipiscing dolore ut sed sit. sed sit aliquam sit dolore sed dolor dolor dolor. nonummy nibh diam laoreet aliquam sit tincidunt nibh consectetuer. diam sed amet sed dolore erat diam erat erat.

    2. ipsum ut lorem laoreet.

      sed dolor consectetuer aliquam aliquam dolor dolore erat ipsum dolor sed dolor. ipsum laoreet nonummy amet erat erat erat adipiscing aliquam ut magna diam.

    3. diam dolore sed lorem consectetuer.

      sit sit diam consectetuer consectetuer erat lorem. sed dolore nibh dolor sit ut nibh. nonummy lorem laoreet euismod laoreet ipsum ut. consectetuer dolore lorem ipsum diam elit dolor.

    4. lorem elit euismod.

      tincidunt tincidunt elit aliquam consectetuer lorem aliquam laoreet tincidunt. erat aliquam adipiscing elit amet euismod adipiscing euismod diam.

      amet dolore euismod magna dolore ut elit ipsum laoreet. ipsum amet diam nibh ipsum erat sed dolor sed. amet aliquam amet elit diam diam dolore amet magna.

  • Comparable Materials

    *See Terms of Use Below

Information provided by GlueSpec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
20 to 25°C Cure Time Test Method
150°C Cure Time Test Method
150°C Cure Time Test Method
23°C approximately
20 to 25°C Cure Time Test Method
40°C Cure Time Test Method
55°C Cure Time Test Method
75°C Cure Time Test Method
100°C Cure Time Test Method
Cure Time Test Methods
Cure Time Test Method
3.00 min Cure Time Test Method
60 min Cure Time Test Method
1,440 min approximately
4,320 min Cure Time Test Method
300 min Cure Time Test Method
120 min Cure Time Test Method
30 min Cure Time Test Method
15 min Cure Time Test Method
Tensile Strength Test Methods
Tensile Strength Test Method
730 psi CTM 0137A, ASTM D412, When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150oC (302oF), post-cured one hour at 150oC (302oF) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab.
Dielectric Constant Test Methods
Dielectric Constant Test Method
3.01 When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0112, ASTM D150, at 100Hz
3.00 When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0112, ASTM D150, at 100kHz
Dielectric Strength Test Methods
Dielectric Strength Test Method
Excellent Dielectric Strength Test Method
575 V/mil When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0114, ASTM D149
Dissipation Factor Test Methods
Dissipation Factor Test Method
9x10(-4) When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0112, ASTM D150, 100 Hz
10x10(-4) When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0112, ASTM D150, 100 KHz
Volume Resistivity Test Methods
Volume Resistivity Test Method
2e15 (Ohm.cm) When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0249, ASTM D257
Surface Resistivity Test Methods
Surface Resistivity Test Method
>7e16 (ohm) When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0249, ASTM D257
Elongation Test Methods
Elongation Test Method
470 % When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab, CTM 0137A, ASTM D412
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
30 When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150°C (302°F), post-cured one hour at 150°C (302°F) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab.
Density Test Methods
Density Test Method
0.00 g/cm³ Relative, Press cured only, When 100 parts of SILASTIC MDX4-4210 BioMedical Grade Elastomer and 10 parts of the curing agent are mixed, de-aired, press-cured for 3 minutes at 150oC (302oF), post-cured one hour at 150oC (302oF) and stabilized for three hours at room temperature, the typical properties will be obtained on a 0.075-inch slab.